METAL REPAIR COMPOUNDS

SEALXPERT PS102 STAINLESS STEEL REPAIR PUTTY

FEATURES:

  • Metal-filled two-component epoxy putty
  • Bonds to metals, concrete and plastics
  • Cures at room temperature
  • Can be drilled, tapped, machined or painted
  • Excellent resistance to oil, gasoline, water and chemicals
  • Ideal for patching and repairing areas where welding or brazing is undesirable

APPLICATION:

  • Suitable for repairing defects and rebuilding of steel and iron casting parts
  • Recommended for repairing and rebuilding of worn components such as bearing and fan housing

SEALXPERT PS102 STEEL REPAIR PUTTY

2-part steel-filled epoxy putty used as an adhesive for repairing, filling, high strength bonding and rebuilding on metal and non-metal surfaces, cured to a tough, durable and rigid compound

PACKAGE:

  • 454 gram/set

SEALXPERT PS103 ALUMINIUM REPAIR PUTTY

FEATURES:

  • Aluminium -filled two-component epoxy putty
  • Repairs to non-rusting aluminium castings, machinery and equipment
  • Excellent resistance to chlofluorocarbons
  • Bonds to aluminium and other metals
  • Fills porosity in aluminium castings
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for rebuilding of various aluminium casting parts
  • Used for repairing aluminium casting air holes and sand holes, shrinkage and cracks
  • Used for filling oversize, scratch or damaged repairing
  • Applicable to general machines, automobiles, airplanes, watercraft etc.

SEALXPERT PS103 ALUMINIUM REPAIR PUTTY

2 part epoxy putty heavily reinforced with aluminium powder used for fairing, bonding, repairing, rebuilding or patching aluminium parts, castings and equipment

PACKAGE:

  • 454 gram/set

SEALXPERT PS104 BRONZE REPAIR PUTTY

FEATURES:

  • Bronze -filled two-component epoxy putty.
  • Repairs to bronze and brass bushings, shafts, castings and parts
  • Repairs and rebuilds area where brazing is undesirable or impossible
  • Bonds securely to bronze alloys, brass, copper and ferrous metals
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for rebuilding and repairing of various bronze casting parts
  • Used for repairing bronze casting air holes and sand holes, shrinkage and cracks
  • Used for filling oversize, scratch or damaged repairing
  • Applicable to watercrafts, machines, automobiles, mining machineries etc.

SEALXPERT PS104 BRONZE REPAIR PUTTY

Bronze filled epoxy compound with bronze powder used as cold welding, bonding, patching, filling, bonding and rebuilding of bronze parts, castings and equipment

PACKAGE:

  • 227 gram/set

SEALXPERT PS105 STAINLESS STEEL REPAIR PUTTY

FEATURES:

  • Stainless steel-filled two-component epoxy putty
  • Patch, repair and rebuild stainless steel parts and equipment
  • Bonds to ferrous and non-ferrous metals
  • Non-rusting

APPLICATION:

  • Used for repairing stainless steel and steel parts defect repairing and worn part rebuilding
  • Applicable to watercrafts, machines, automobiles, mining machineries etc.

SEALXPERT PS105 STAINLESS STEEL REPAIR PUTTY

Stainless steel-filled epoxy compound that cures at room temperature to form a hard and durable finish on damaged stainless steel surfaces and equipment

PACKAGE:

  • 454 gram/set

SEALXPERT PS106 UNDERWATER REPAIR PUTTY

FEATURES:

  • Ceramic-based two-component epoxy putty.
  • Suitable for moist and wet conditions
  • Excellent resistance to oil and chemicals
  • Bonds to metallic and non-metallic surfaces
  • Fills porosity and cracks on valves and pump bodies
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for repairing pipeline, valve, pump shell, tank body and concrete under emergency
  • Used for leakage stopping for water machineries, watercrafts repairing, mines and buildings etc.
  • Used in splash zone repair in combination of SealXpert Fiberglass Repair Tapes

SEALXPERT PS106 UNDERWATER REPAIR PUTTY

Fibreglass reinforced polymer compound for permanent repair, patching, rebuilding, bonding to many surfaces in wet and underwater applications

PACKAGE:

  • 454 gram/set

SEALXPERT PS107 5 MIN (SF) REPAIR PUTTY

FEATURES:

  • Fast-curing
  • Stainless steel-filled two-component epoxy putty
  • Suitable for quick and emergency repairs
  • Cures in less than one hour
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for emergency and quick repairing of steel, iron, stainless steel etc. metal damaged parts, worn parts and leakage
  • Applicable to watercrafts, machines, automobiles, mining machineries etc.

SEALXPERT PS107 5 MIN (SF) REPAIR PUTTY

Super fast-curing, steel-filled epoxy compound general purpose adhesive for emergency quick repairs that sets in 5 minutes, eliminates the need for welding and brazing

PACKAGE:

  • 454 gram/set

SEALXPERT PS108 HI-TEMP REPAIR PUTTY

FEATURES:

  • Withstands high temperature up to 230 °C (446 °F) (continuous) and 280 °C (536 °F) (intermittent)
  • Nickel alloy-filled two-component epoxy putty
  • Suitable for engine parts repairs
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for repairing abrasion, scratch, and crack etc. on equipment operating at high temperature
  • Applicable to watercrafts, automobiles, machineries in petrochemical, power plant etc.

SEALXPERT PS108 HI-TEMP REPAIR PUTTY

High temperature resistance repair putty for adhesion, filling, repair and rebuilding for exhaust system with excellent adhesion to cast iron

PACKAGE:

  • 454 gram/set

 

SEALXPERT PS109 SUPERMETAL EPOXY PUTTY

FEATURES:

  • Alloy and ceramic filled two-component epoxy putty
  • Excellent hardness
  • Cold welding repairing material
  • Versatile durable repair composite
  • Outstanding adhesion to all metals
  • Excellent corrosion resistance
  • Superior chemical resistance
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Suitable for repairing worn rotating shafts
  • Applicable for making repairs that can be precision machined

SEALXPERT PS109 SUPERMETAL EPOXY PUTTY

Two component ceramic and steel reinforced polymer putty compound, with excellent strength for repairing and rebuilding worn and damaged rotating shafts

PACKAGE:

  • 454 gram/set

SEALXPERT PS110 TITANIUM REPAIR PUTTY

FEATURES:

  • Titanium filled two-component epoxy putty
  • High performance
  • Excellent chemical resistance
  • Withstands heavy loads in harsh chemical environments
  • Can be drilled, tapped, machined or painted.

APPLICATION:

  • Suitable for repairing and rebuilding on load bearing components
  • Applicable for repairs to machineries and equipment that can be precision machined.

TECHNICAL DATA:

Product No.ColourCompressive Strength
psi
(kg/cm2)
Tensile Strength
psi
(kg/cm2)
Shear Strength
psi
(kg/cm2)
Hardness
Shore D
Temperature Range°C(°F)Mixture (A:B)Pot Life
min
Curing TimeCoverage Area
(per set)
cm2 at 0.2″ (6 mm) thickness
WeightVolume50% load
hour
100% load
hour
PS 102Grey18130
(1275)
4931
(347)
2901
(204)
80-50 to 160
(-58 to 320)
9:15:140824450
PS 103Aluminium14214
(999)
4351
(306)
2611
(184)
80-50 to 160
(-58 to 320)
6:13.5:1501224503
PS 104Bronze13779
(969)
4351
(306)
2611
(184)
80-50 to 170
(-58 to 338)
9:13:140824165
PS 105Dark Grey15229
(1071)
4931
(347)
2901
(204)
80-50 to 160
(-58 to 320)
11:13.75:1501224465
PS 106Brown13053
(918)
4496
(316)
2611
(184)
80-50 to 150
(-58 to 302)
5:13.5:120612472
PS 107Dark Grey13053
(918)
3626
(255)
2611
(184)
80-50 to 120
(-58 to 248)
1.7:11:151/61450
PS 108Dark Grey12908
(908)
4351
(306)
2611
(184)
80-50 to 280
(-58 to 536)
5:14:160612432
PS 109Dark Grey24656
(1733)
7977
(56)
3046
(214)
90-50 to 160
(-58 to 320)
2:12:1501224450
PS 110Dark Grey18855
(1326)
4061
(286)
2031
(143)
87-50 to 160
(-58 to 320)
11:13.75:121816450

FIRST STAGE: SURFACE PREPARATION


Clean surface thoroughly with solvent

Grit blast surface area with a course file / sandpaper / coarse wheel / abrasive disc pad Clean the surface again with solvent

SECOND STAGE: MIXTURE


Mix component A (Resin) and component B (Hardener) in accordance to the specified ratio

Continuously scrape material from the sides and bottom of st_container until uniform, streak-free consistency is obtained

THIRD STAGE: APPLICATION


Dispense the mixture to prepared surface with trowel

Allow curing in accordance to the minimum curing time at room temperature before operation

SEALXPERT PS110 TITANIUM REPAIR PUTTY

Super alloy titanium-reinforced epoxy compound for precision machined repairs to machinery and equipment. Withstands heavy loads in hard chemical environments

PACKAGE:

  • 454 gram/set

PL102 STEEL REPAIR LIQUID

FEATURES:

  • Steel filled, liquid epoxy
  • Low viscosity, self-levelling liquid
  • Castable
  • Machinable to metallic finish
  • Low shrinkage
  • Resistant to chemicals and most acids, bases, solvents and alkalis

APPLICATION:

  • Casting of steel components
  • Holding fixtures for intricate parts
  • Filling and levelling equipment
  • Repairing hard to reach areas where a flowable epoxy is needed
  • Duplicating or tracing masters
  • Short run dies and moulds

TECHNICAL DATA:

Adhesive tensile shear:2,800 psi (197 kg/cm2)
Tensile strength:3,220 psi (227 kg/cm2)
Compressive strength:10,196 psi (717 kg/cm2)
Modulus of elasticity:274,992 psi (19,334 kg/cm2)
Dielectric strength:1,181 volts/mm
Flexural strength:6,000 psi (394 kg/cm2)
Hardness:85 Shore D

PL102 STEEL REPAIR LIQUID

Two-part low viscosity self-levelling liquid metal repair epoxy for bonding between various metals, crack repair and rebuild, casting of steel components

PACKAGE:

  • 500 gram

PL103 ALUMINIUM REPAIR LIQUID

FEATURES:

  • Can be machined, drilled, or tapped
  • Aluminium filled pourable epoxy

APPLICATION:

  • Used for mould-making, patterns, holding fixtures, levelling equipment
  • Casting of aluminium components

TECHNICAL DATA:

Pot life(100G@25°C): 75 min
Dielectric strength: 4 KV/mm
Adhesive tensile shear: 2,698 psi (190 kg/cm2)
Compressive strength: 9,863 psi (694 kg/cm2)
Hardness: 85 Shore D

PL103 ALUMINIUM REPAIR LIQUID

Two-part low viscosity self-levelling liquid aluminium repair epoxy for bonding between various metals, crack repair and rebuild, casting of aluminium components

PACKAGE:

  • 500 gram